The Perforation Resistance of Aluminum-Based Thermoplastic FMLs

Nassier A. Nassir, R. S. Birch, W. J. Cantwell, M. Al Teneiji, Z. W. Guan

Research output: Contribution to journalArticlepeer-review

13 Scopus citations

Abstract

The perforation resistance of fibre metal laminates (FMLs) made of an S-glass fibre reinforced poly-ether-ketone-ketone (GF/PEKK) composite and an aluminium alloy (2024-T3) is investigated. Initial attention is focused on assessing the effect of the processing temperature on the tensile strength of the aluminium alloy. Here, it has shown that the processing cycle results in a reduction of approximately 35% in both the tensile strength and yield strength of the aluminium alloy. A comparison of the quasi-static and dynamic perforation responses of the FMLs highlighted the rate-sensitivity of these laminates, with the perforation energy increasing as the loading rate varies from quasi-static to impact. After testing, the FML specimens were sectioned to highlight the prevailing failure modes. An examination of the cross-sections indicated that the impact energy of the projectile is absorbed through plastic deformation and tearing of the metal layers, delamination between the composite plies and metal layers as well as fibre fracture. Finite element models (FEM), using ABAQUS/Explicit, have been developed to predict the behaviour of the FMLs subjected to dynamic loading. The outputs of the FE models were then validated against the measured experimental force–displacement traces and the observed failure modes. The results of the FE models were in a good agreement with the experimental data, in terms of the initial stiffness, maximum force and maximum displacement, as well as the perforation mechanisms.

Original languageBritish English
Pages (from-to)587-605
Number of pages19
JournalApplied Composite Materials
Volume28
Issue number3
DOIs
StatePublished - Jun 2021

Keywords

  • Aluminium alloy
  • Fibre metal laminates
  • Finite element
  • Impact loading
  • Perforation
  • Poly-ether-ketone-ketone

Fingerprint

Dive into the research topics of 'The Perforation Resistance of Aluminum-Based Thermoplastic FMLs'. Together they form a unique fingerprint.

Cite this