TY - JOUR
T1 - Comparative scuffing performance and chemical analysis of metallic surfaces for air-conditioning compressors in the presence of environmentally friendly CO2 refrigerant
AU - Nunez, Emerson Escobar
AU - Demas, Nicholaos G.
AU - Polychronopoulou, Kyriaki
AU - Polycarpou, Andreas A.
N1 - Funding Information:
This research work was supported by the 29 member companies of the Air-Conditioning and Refrigeration Center, an Industry-University Cooperative Research Center at the University of Illinois at Urbana-Champaign. Chemical analyses were performed at the Center for Microanalysis of Materials, University of Illinois at Urbana-Champaign, which is partially supported by the U.S. Department of Energy under grant DEFG02-91-ER45439 .
PY - 2010/2/11
Y1 - 2010/2/11
N2 - Carbon dioxide (CO2) has received significant interest as an alternative refrigerant for air-conditioning compressors due to its environmental benefits. These environmental benefits include zero ozone depletion potential and minimal global warming potential compared to commonly used hydrochlorofluorocarbon and hydrofluorocarbon refrigerants. This study presents results for three typical metallic tribopairs commonly found in air conditioning compressors, namely, Al390-T6, gray cast iron, and Mn-Si brass against 52,100 steel pins. The experiments were performed using a specialized tribometer capable of simulating compressor conditions, and in the presence of CO2 and polyalkylene glycol lubricant. It was found that the scuffing resistance of gray cast iron and Mn-Si brass was similar and both materials performed better than Al390-T6. Through scanning electron microscopy and energy dispersive spectroscopy it was found that lead in Mn-Si brass melted during scuffing, and prevented sudden catastrophic failure of Mn-Si brass, unlike gray cast iron and Al390-T6 which failed abruptly. X-ray photoelectron spectroscopy conducted on the worn surfaces showed that chemically different species were present on the surfaces and their lubricious effect, originating from different metal oxides, could explain the scuffing behavior of the investigated alloys.
AB - Carbon dioxide (CO2) has received significant interest as an alternative refrigerant for air-conditioning compressors due to its environmental benefits. These environmental benefits include zero ozone depletion potential and minimal global warming potential compared to commonly used hydrochlorofluorocarbon and hydrofluorocarbon refrigerants. This study presents results for three typical metallic tribopairs commonly found in air conditioning compressors, namely, Al390-T6, gray cast iron, and Mn-Si brass against 52,100 steel pins. The experiments were performed using a specialized tribometer capable of simulating compressor conditions, and in the presence of CO2 and polyalkylene glycol lubricant. It was found that the scuffing resistance of gray cast iron and Mn-Si brass was similar and both materials performed better than Al390-T6. Through scanning electron microscopy and energy dispersive spectroscopy it was found that lead in Mn-Si brass melted during scuffing, and prevented sudden catastrophic failure of Mn-Si brass, unlike gray cast iron and Al390-T6 which failed abruptly. X-ray photoelectron spectroscopy conducted on the worn surfaces showed that chemically different species were present on the surfaces and their lubricious effect, originating from different metal oxides, could explain the scuffing behavior of the investigated alloys.
KW - Al390-T6
KW - Carbon dioxide refrigerant
KW - Compressors
KW - Gray cast iron
KW - Mn-Si brass
KW - Scuffing
UR - http://www.scopus.com/inward/record.url?scp=74649086392&partnerID=8YFLogxK
U2 - 10.1016/j.wear.2009.11.002
DO - 10.1016/j.wear.2009.11.002
M3 - Article
AN - SCOPUS:74649086392
SN - 0043-1648
VL - 268
SP - 668
EP - 676
JO - Wear
JF - Wear
IS - 5-6
ER -